General purpose PC/ABS

General purpose PCABS alloy

High flow and high impact
Used in electrical and electronic, automotive, household goods, thin-walled parts, etc.

Physical Properties of Products

Property

Melt index
Mold shrinkage
Tensile Strength
Elongation at break
Elongation at break
Flexural modulus
Cantilever beam notched impact
Cantilever beam notched impact
Vicat softening point temperature
Flame retardant performance
Flame retardant performance
Volume resistivity
density

Property

ASTM D1238
ASTM D955
ASTM D638
ASTM D638
ASTM D790
ASTM D790
ASTM D256
ASTM D648
ASTMD1525
UL 94
IEC 60093
IEC 60093
ASTM D792

Testing condition

260℃2.16kg

260℃5kg

3.2mm
50mm/min
50mm/min
2mm/min
2mm/min

3.2mm 23℃

3.2mm -30℃

1.82Mpa
50N 120℃/h
1.6mm
-
-
23℃

Unit

g/10min

g/10min

%
Mpa
%
Mpa
Mpa
J/m
Class
Ω
Ω•m
kg/m3

A6110

6

18

0.5-0.7
58
80
80
2300

650

450

110
135
HB
1.00E+16
1.00E+14
1190

A6120

10

30

0.5-0.7
56
80
80
2300

640

440

107
130
HB
1.00E+16
1.00E+14
1150

A6130

10

31

0.5-0.7
56
80
80
2300

680

430

102
122
HB
1.00E+16
1.00E+14
1130

A6140

9.9

32

0.5-0.7
55
80
80
2300

608

420

99
118
HB
1.00E+16
1.00E+14
1124

A6150

10.2

34

0.5-0.7
53
80
80
2300

530

420

92
110
HB
1.00E+16
1.00E+14
1117
  • The above data is measured with a sample at 23 ° C and a temperature of 50%. The data is typical for the experiment and no formal warranty is promised.
  • Color product data may change slightly
Plastic Processing Technology
Processing technology
A6110
A6120
A6130
A6140
A6150
Barrel temperature
Nozzle
260~290℃
250~270℃
250~270℃
250~270℃
250~270℃
Barrel temperature
Anterior segment
250~285℃
245~265℃
245~265℃
245~265℃
245~265℃
Barrel temperature
Middle part
250~280℃
245~265℃
245~265℃
245~265℃
245~265℃
Barrel temperature
Posterior segment
240~270℃
240~260℃
240~260℃
240~260℃
240~260℃
Temperature of Die
60~90℃
60~90℃
60~90℃
60~90℃
60~90℃
Backpressure pressure
0.35~1.00Mpa
0.35~1.00Mpa
0.35~1.00Mpa
0.35~1.00Mpa
0.35~1.00Mpa
Screw speed
25-75Rpm
25-75Rpm
25-75Rpm
25-75Rpm
25-75Rpm
Drying temperature
100~110℃
100~110℃
100~110℃
100~110℃
100~110℃
Drying time
4h
4h
4h
4h
4h
  • The above process parameters are for reference only, and should be adjusted according to the product, injection molding machine and mold.